Wironit® extrahart
The ideal partial denture alloy for combination work
- Due to its high proof strength and ultimate strength, this alloy is ideally suited for combination work
- Outstanding casting properties thanks to the special composition with silicon and carbon
- Very low thermal conductivity of the alloy emphasises the wearing comfort of the prosthesis
- Biocompatible and corrosion-resistant
| Composition in % by mass |
|---|
| Co 63.0 · Cr 30.0 · Mo 5.0 · Si 1.0 · Mn 1.0 · C |
| Alloy characteristics | Standard values |
|---|---|
| Type (ISO 22674) | 5 |
| Density | 8.2 g/cm3 |
| Preheating temperature | 950–1050 °C |
| Solidus, liquidus temperature | 1260, 1390 °C |
| Casting temperature approx. | 1420 °C |
| Young’s modulus | 185 GPa |
| Proof strength (Rp0.2) | 635 MPa |
| Elongation after fracture (A5) | 8% |
| Vickers hardness | 385 HV10 |
ISO 22674
| Availability | Contents | REF |
|---|---|---|
| Wironit® extrahart | 1000 g | 50060 |
| Wironit® extrahart | 250 g | 50050 |
ISO 22674
| Accessories | Contents | REF |
|---|---|---|
| Wiroweld CoCr laser wire, carbon-free, Ø 0.35 mm | 2 m – 1,5 g | 50003 |
| Wiroweld CoCr laser wire, carbon-free, Ø 0.5 mm | 1.5 m – 2 g | 50005 |
| Cobalt-chrome solder | 4g | 52520 |
ISO 22674
Downloads
Contact / Service
BEGO USA Inc.
24 Albion Road
Suite 103
Lincoln, RI 02865
BEGO Order:
Phone: 401-334-9261
Email: begoorders@begousa.com
BEGO Product Info:
Phone: 401-334-9261
Email: begoinfo@begousa.com
BEGO Service:
Phone: 401-475-3196
Email: begoservice@begousa.com
Pictures and illustrations are exemplary. Colors, symbols, design, and information on the labels and/or packaging shown may differ from reality.